A micromechanism study of thermosonic gold wire bonding on aluminum pad

H. Xu*, C. Liu, V. V. Silberschmidt, S. S. Pramana, T. J. White, Z. Chen, M. Sivakumar, V. L. Acoff

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

65 Citations (Scopus)

Abstract

A micromechanism of thermosonic gold wire bonding was elaborated by examining its interfacial characteristics as a result of the bonding process, including the fragmentation of the native aluminum oxide layer on Al pads, and formation of initial intermetallic compounds (IMCs). It is found that the existence of an approximately 5 nm thick native oxide layer on original Al pads has a significant effect on the bonding, and the nucleation of IMCs during the bonding process must overcome this relatively inert thin film. Bonding strength was fundamentally determined by the degree of fragmentation of the oxide films, through which the formation of IMCs can be initiated due to the direct contact of the metal surfaces to be bonded. The extent of fracture the oxide layer was strongly influenced by the level of ultrasonic power, as at its high level alumina fragmentation becomes pervasive resulting in contiguous alloy interfaces and robust bonds. The IMCs formed at the interfaces were identified as Al 4 Al and AuAl2 with a thickness of 150-300 nm. The formation mechanism of such IMCs was explained by the effective heat of formation theory.

Original languageEnglish
Article number113517
JournalJournal of Applied Physics
Volume108
Issue number11
DOIs
Publication statusPublished - Dec 1 2010
Externally publishedYes

ASJC Scopus Subject Areas

  • General Physics and Astronomy

Fingerprint

Dive into the research topics of 'A micromechanism study of thermosonic gold wire bonding on aluminum pad'. Together they form a unique fingerprint.

Cite this