Influences of graphene oxide support on the electrochemical performances of grapheme oxide-MnO₂ nanocomposites

MnO₂ supported on graphene oxide (GO) made from different graphite materials has been synthesized and further investigated as electrode materials for supercapacitors. The structure and morphology of MnO₂-GO nanocomposites are characterized by X-ray diffraction, X-ray photoemission spectroscopy, scanning electron microscopy, transmission electron microscopy, Raman spectroscopy, and Nitrogen adsorption-desorption. As demonstrated, the GO fabricated from commercial expanded graphite (denoted as GO(1)) possesses more functional groups and larger interplane gap compared to the GO from commercial graphite powder (denoted as GO(2)). The surface area and functionalities of GO have significant effects on the morphology and electrochemical activity of MnO₂, which lead to the fact that the loading amount of MnO₂ on GO(1) is much higher than that on GO(2). Elemental analysis performed via inductively coupled plasma optical emission spectroscopy confirmed higher amounts of MnO₂ loading on GO(1). As the electrode of supercapacitor, MnO₂-GO(1) nanocomposites show larger capacitance (307.7 F g^-1) and better electrochemical activity than MnO₂-GO(2) possibly due to the high loading, good uniformity, and homogeneous distribution of MnO₂ on GO(1) support.