Microstructure and composition analysis in plasma sprayed coatings of Al₂O₃/ZrSiO₄ mixtures

Plasma spraying of Al₂O₃/ZrSiO₄ was performed using spray dried and plasma spheroidised powder feedstock. The mixtures were sprayed using different spray stand-off distances and plasma power levels. X-Ray diffraction (XRD) was used to characterise the phase composition and scanning electron microscopy (SEM) examined the morphology of the sprayed surface and polished cross-sections. The results showed that the plasma spray process parameters played an important role in the final outcome of microstructures of the coatings. The coatings produced with spheroidised powders displayed a much denser structure than those produced with the spray-dried powders. The phase composition analysis showed the presence of amorphous phases in addition to crystalline alumina, zircon and tetragonal (t) zirconia (ZrO₂). Transmission electron microscopy (TEM) showed that amorphous phases and t-ZrO₂ crystals with particle size ∼ 100-200 nm could coexist within a single splat due to the relatively low local cooling rate.